Enhanced Perpendicular Exchange Bias in Co/Pd Antidot Arrays

Artikel i vetenskaplig tidskrift
Författare T Nguyen
J. Fedotova
J. Kasiuk
W. B. Wu
J. Przewoznik
C. Kapusta
O. Kupreeva
S. Lazarouk
T. H. T. Trinh
K. T. Do
H. M. Do
D. L. Vu
Johan Åkerman
Publicerad i Journal of Electronic Materials
Volym 48
Nummer/häfte 3
Sidor 1492-1497
ISSN 0361-5235
Publiceringsår 2019
Publicerad vid Institutionen för fysik (GU)
Sidor 1492-1497
Språk en
Länkar dx.doi.org/10.1007/s11664-018-06847...
Ämnesord Multilayered Co/Pd thin films, porous TiO2 templates, perpendicular magnetic anisotropy, exchange, magnetic-properties, templates, A (reprint author), Royal Inst Technol, Mat Phys Dept, S-16440 Kista, Sweden., Nguyen, TNA (reprint, Engineering, Materials Science, Physics
Ämneskategorier Fysik

Sammanfattning

Magnetic nanostructures revealing the exchange bias (EB) effect have attracted much interest in recent years due to their promising applications in spintronics, magneticsensing and recording devices with various functionalities. In this paper, we report on the perpendicular exchange bias effect in a multilayered thin film composed of [Co/Pd] ferromagnetic multilayers exchange-coupled to an antiferromagnetic IrMn. The film was deposited on a porous anodized titania template. Influences of the films' surface morphology as well as the order of layers deposited on the EB effect were studied. The enhancements of the EB field H-EB (up to 30%) and the coercive field H-C (two times) were achieved in the nanoporous films relative to their continuous film counterparts, which could be attributed to the specific morphology of the porous surfaces.