The use of MgO-paste as a biodegradeable bone cement

Paper i proceeding
Författare A. Biel
Mobina Chaudhry
Stefan Gustafsson
Håkan Nygren
Publicerad i Materials Today-Proceedings
Volym 3
Nummer/häfte 2
Sidor 556-561
ISSN 2214-7853
Publiceringsår 2016
Publicerad vid Institutionen för biomedicin
Sidor 556-561
Språk en
Länkar dx.doi.org/10.1016/j.matpr.2016.01....
Ämnesord Bone formation, bone cement, Magnesium, bone healing, osteoporosis, magnesium
Ämneskategorier Klinisk medicin

Sammanfattning

The use of MgO-paste as bone cement was tested on titanium cylinders implanted into rat tibia. The evaluation of bone healing was made with the retention force (pull-out) test, light microscopy and ESEM/EDX. Preimplantation of the MgO-paste into drill perforations of rat tibia increased the retention of the titanium implant 6-fold. The error was expressed as the 95% confidence interval of means (n = 10 bones in each group). The observed difference between 3.46+/-0.71 N/mm(2) for Ti-cylinders implanted with MgO-paste and 0.56+/-0.26 N/mm(2) for Ti-cylinders implanted directly into the bone, is statistically significant (p < 0.01). The increase of retention force, caused by MgO is parallel to an increased thickness of the compact bone surrounding the implant and closer contact between bone and implant. Histological examination of the implant-related bone showed that the MgO-induced bone growth is mediated by the formation of a bone-inducing matrix. The matrix contains organic substance, most likely proteins.