Graded Anisotropy FePtCu Films

Artikel i vetenskaplig tidskrift
Författare Randy K. Dumas
Chaolin Zha
Yeyu Fang
Valentina Bonanni
J. W. Lau
Josep Nogués
Johan Åkerman
Publicerad i IEEE Transactions on Magnetics
Volym 47
Nummer/häfte 6
Sidor 1580
ISSN 0018-9464
Publiceringsår 2011
Publicerad vid Institutionen för fysik (GU)
Sidor 1580
Språk en
Länkar dx.doi.org/10.1109/TMAG.2010.210274...
Ämnesord magnetism, spintronics, graded materials
Ämneskategorier Magnetism

Sammanfattning

The fabrication and subsequent analysis of continuously graded anisotropy films are discussed. During deposition, a compositional gradient is first achieved by varying the Cu concentration from Cu-rich (Fe53Pt47)70Cu30 to Cu-free Fe53Pt47. The anisotropy gradient is then realized after thermal post-annealing, and by utilizing the strong composition dependence of the low-anisotropy (A1) to high-anisotropy (L10) ordering temperature. The magnetic properties are investigated by surface sensitive magneto-optical Kerr effect and alternating gradient magnetometer (AGM) measurements. AGM first-order reversal curve (FORC) measurements are employed in order to provide a detailed analysis of the reversal mechanisms, and therefore the induced anisotropy gradient. At low annealing temperatures, the FORC measurements clearly indicate the highly coupled reversal of soft and hard phases. However, significant interdiffusion results in virtually uniform films at elevated annealing temperatures. Additionally, the A1 to L10 ordering process is found to depend on the film thickness.