Bone response to laser-induced micro- and nano-size titanium surface features.

Artikel i vetenskaplig tidskrift
Författare Rickard Brånemark
Lena Emanuelsson
Anders Palmquist
Peter Thomsen
Publicerad i Nanomedicine : nanotechnology, biology, and medicine
ISSN 1549-9642
Publiceringsår 2011
Publicerad vid Institutionen för kliniska vetenskaper, Avdelningen för biomaterialvetenskap
Institutionen för kliniska vetenskaper, Avdelningen för ortopedi
Språk en
Länkar dx.doi.org/10.1016/j.nano.2010.10.0...
Ämneskategorier Biomaterialvetenskap, Klinisk medicin

Sammanfattning

The present study explored whether laser-induced, site-specific implant surface modifications with micro- and nano-scale topography were able to promote bone formation. The aim was to evaluate the biomechanical and histological response to partly laser-modified titanium implants compared with machined implants. After an early 8-week healing period in rabbit tibia and femur, a 250% increase in removal torque was demonstrated for the partly laser-modified surface. Further, different fracture mechanisms were demonstrated for the two surfaces. Histologically, significantly more bone was found in direct contact with the laser-modified surface for the implants in the tibia sites, while a similar amount of bone tissue was observed in contact with the implant in the femoral sites. In conclusion, an improved bone-implant interface anchorage was promoted by an increase in micro- and nano-scale implant surface topography and surface oxide induced by topological laser treatment.