Magnetization reversal of antiferromagnetically coupled (Co/Ni) and (Co/Pt) multilayers

Artikel i vetenskaplig tidskrift
Författare A. Al Subhi
R. Sbiaa
Mojtaba Ranjbar
Johan Åkerman
Publicerad i Journal of Magnetism and Magnetic Materials
Volym 479
Sidor 27-31
ISSN 0304-8853
Publiceringsår 2019
Publicerad vid Institutionen för fysik (GU)
Sidor 27-31
Språk en
Länkar dx.doi.org/10.1016/j.jmmm.2019.02.0...
Ämnesord perpendicular-anisotropy, media, layers, spin
Ämneskategorier Magnetism

Sammanfattning

Magnetization reversal and magnetic exchange coupling of (Co/Ni)( x N)/Ru/(Co/Pt)(x12) were investigated as a function of the temperature. The number of repeats N of the soft multilayer (Co/Ni) was varied from 4 to 8 bilayers while the number of repeats of the hard bilayers (Co/Pt) was fixed to 12. Two steps hysteresis loops were observed for coupled structure with only 4 repeats of (Co/Ni) in a wide range of temperature (25-300 K). From the shift of the minor hysteresis loop, the antiferromagnetic exchange coupling H-ex was measured and then the interlayer exchange coupling J(ex) was calculated. A non-monotonous dependence of J(ex) with temperature was observed for N = 4 with a maximum J(ex) of 0.13 erg/cm(2) at 150 K. The annealing process performed on the same structure confirms the unusual behavior of interlayer exchange coupling J(ex). As the repetition number N increases to 8 bilayers the two steps hysteresis loops disappeared in the investigated temperature range, however a small kink appeared in the range of 125 and 225 K for the case of 6 bilayers. From the analysis of the coupled and uncoupled structures, it seems that the dipolar energy overcomes the antiferromagnetic coupling for thicker (Co/Ni) multilayer.

Sidansvarig: Webbredaktion|Sidan uppdaterades: 2012-09-11
Dela:

På Göteborgs universitet använder vi kakor (cookies) för att webbplatsen ska fungera på ett bra sätt för dig. Genom att surfa vidare godkänner du att vi använder kakor.  Vad är kakor?

Denna text är utskriven från följande webbsida:
http://www.gu.se/forskning/publikation/?publicationId=278468
Utskriftsdatum: 2019-11-15